| IEC designation | U100B/146 | U100B/127 | |
| Diameter D | mm | 255 | 255 |
| Height H | mm | 146 | 127 |
| Creepage distance L | mm | 320 | 320 |
| Socket coupling | mm | 16 | 16 |
| Mechanical failing load | kn | 100 | 100 |
| Mechanical routine test | kn | 50 | 50 |
| Wet power frequency withstand voltage | kv | 40 | 40 |
| Dry lightning impulse withstand voltage | kv | 100 | 100 |
| Impulse puncture voltage | P.U | 2.8 | 2.8 |
| Power frequency puncture voltage | kv | 130 | 130 |
| Radio influence voltage | μv | 50 | 50 |
| Corona visual test | kv | 18/22 | 18/22 |
| Power frequency electric arc voltage | ka | 0.12s/20kA | 0.12s/20kA |
| Net weight per unit | kg | 4 | 4 |
Performance of glass insulator
1.1 Characteristics of components
The characteristics of disc-type suspension insulator elements shall conform to GB/T 7253.
1.2 Dimensional Deviation
The dimensions of the test insulators shall conform to the corresponding drawings, paying particular attention to any dimensions with special public requirements (e.g., specified structural height) and details affecting interchangeability (e.g., connection dimensions as specified in GB/T 4056).
A) Unless otherwise agreed, for all dimensions not marked with a specific deviation, the following deviations (d is the inspection dimension, in units; Mm);
Soil (0.04d+1.5) mm, when D ≤300mm and all lengths of creepage distance; ± (0.025d +6) mm, when D >300mm;
The deviation given above applies even if the creepage distance is specified as a nominal value of the stack small.
B) The structural height deviation of insulators is ± 0.024nh (n represents 6 insulators). For 330kV and above the use of the absolutely
Edge, the structural height deviation of 6 insulator strings shall not exceed ±19mm. C) The change gauge of the axial measuring device shall be set at 4% of the insulator’s nominal diameter;
The change gauge for the radial measuring device is set at 3% of the insulator’s nominal diameter.
1.3 Insulators
The appearance quality of the porcelain shall comply with the provisions of Chapter 28 of GBT 772-2005 (1.3) and GBT 1001.1-2003 (GBT 1001.1-2003). The surface of the porcelain insulator shall be free from warps, sand holes, bubbles, bumps, external objects and other defects.
The appearance quality of glass parts shall comply with JB/T 9678-1999 Chapter 4 and GB/T1001.1 — 2003 Chapter 28. Insulator glass shall be free from cracks, seams, air bubbles, impurities and other defects, and shall be uniformly tempered on its surface. All exposed glass surfaces shall be light dispersive.
1.4 Iron cap and steel foot
The iron caps of insulators shall comply with JB/T 8178. Insulator pot foot shall comply with JB/T 9677. Caps and feet shall not be made by joining, welding, cold crimping or any other process involving more than one piece of material.
Product detail pictures:
Related Product Guide:
We constantly think and practice corresponding to the change of circumstance, and grow up. We aim at the achievement of a richer mind and body along with the living for Short Lead Time for High Tension Glass Insulator - High Voltage 100kn Disc Suspension Toughened Glass Insulator U100B – Johnson, The product will supply to all over the world, such as: Qatar, Greece, Congo, we rely on own advantages to build a mutual-benefit commerce mechanism with our cooperative partners. As a result, now we have gained a global sales network reaching the Middle East, Turkey, Malaysia and Vietnamese.
By Natalie from Vietnam - 2017.04.08 14:55
High production efficiency and good product quality, fast delivery and completed after-sale protection, a right choice, a best choice.
By Diego from Kenya - 2017.08.21 14:13